Peningkatan Ketahanan Aus pada Baja Tahan Karat Martensitik 13Cr AISI 410 setelah Proses Austenisasi dan Tempering [Improvement of Wear Resistance of 13Cr AISI 410 Martensitic Stainless Steel after Austenitizing and Tempering Process]

Annisa Siti Apriani, Moch. Syaiful Anwar, Rusnaldy Rusnaldy, Efendi Mabruri

Abstract

The turbine blades that were developed from martensitic stainless steel 13Cr are usually operate on high rotation speed in steam power plants and often found to be failures in the material. One of the failure causes is the presence of foreign material that gives the abrasion impact on the surface of the turbine blade. The aim of this study is observed the effect of austenitization and tempering temperatures on the hardness and abrasion resistance of 13Cr martensitic stainless steel. The examinations were carried out i.e. hardness Rockwell C and abrasion resistance. The optimum hardness values obtained on 13Cr martensitic stainless steel which austenitizing at 1050 °C and tempering of 600 °C. The increasing of tempering temperature in the 13Cr stainless steel does not give a linear negative effect on the abrasion resistance of the steel.

Abstrak

Sudu (blade) turbin yang terbuat dari baja tahan karat martensitik 13Cr yang selalu beroperasi pada kecepatan putaran yang tinggi di pembangkit listrik tenaga uap sering ditemukan kegagalan pada material tersebut. Salah satu penyebab kegagalan ini adalah adanya benda asing  yang memberikan dampak abrasi pada permukaan sudu turbin. Penelitian ini bertujuan untuk mengamati pengaruh perlakuan panas austenitization dan tempering terhadap kekerasan dan ketahanan abrasi baja tahan karat martensitik 13Cr. Pengujian yang dilakukan adalah uji kekerasan Rockwell C dan uji ketahanan abrasi. Hasil penelitian ini adalah nilai kekerasan optimum ditemukan pada baja tahan karat martensitik 13Cr yang mengalami austenitization pada suhu 1050°C dengan waktu tempering 600°C. Dengan semakin tinggi suhu tempering maka nilai kekerasan baja tahan karat 13Cr semakin turun. Akan tetapi, kenaikan suhu tempering pada baja tahan karat 13Cr tidak memberikan pengaruh negatif secara linier terhadap ketahanan abrasi baja tersebut.

 

Keywords

Baja tahan karat martensitik 13Cr; sudu turbin uap; austenisasi; tempering; kekerasan; ketahanan aus ; 13Cr martensitic stainless steel; steam turbine blade; austenitizing; tempering; hardness Rockwell C; abrassion resistance

References

Tukesh Kumar Patel, Prakash Kumar Sen, Ritesh Sharma,” Review on common failure of steam turbine blade,” International Journal of Research (IJR)., Volume 2, Issue 11, 137-141, November 2015.

Stephen Rowbotham, Olivia Chung, Monika Ko and Jessica Wong,”Failure Mechanisms Encountered in Geothermal Steam Service,” Proceedings World Geothermal Congress 2015., Melbourne, Australia, 1-8, 19-25 April 2015.

Subramanyam Pavuluri , A. Siva Kumar,” Experimental investigation on design of high pressure steam turbine blade,” International Journal of Innovative Research in Science, Engineering and Technology, Vol. 2, Issue 5, 1469-1476, May 2013.

Ivan Sunit Rout, Abhishek Gaikwad, Vinod Kumar Verma, Mohammad Tariq,”Thermal Analysis of Steam Turbine Power Plants,” IOSR Journal of Mechanical and Civil Engineering (IOSR-JMCE), Volume 7, Issue 2, 28-36, May – Jun 2013.

Akash Deep Kushwaha, Aakash Soni, Lovelesh Garewal,”Critical review paper of steam turbine blades corrosion and its solutions,” International Journal of Scientific Research Engineering & Technology (IJSRET), Volume 3, Issue 4, 776-784, July 2014.

Moch. Syaiful Anwar dan Efendi Mabruri,” Ketahanan aus abrasif dari beberapa jenis modifikasi 13Cr baja tahan karat martensit,” Majalah Metalurgi, 3, 149-154, 2015.

Gunawan Dwi Haryadi,”Pengaruh suhu tempering terhadap kekerasan, kekuatan tarik dan struktur mikro pada baja K-460,” Rotasi, Volume 8 Nomor 2, 1-8, April 2006.

A.Rajasekhar,” Heat treatment methods applied to AISI 431 martensitic stainless steels,” International Journal of Scientific & Engineering Research, Volume 6, Issue 4, 547-553, April-2015

Copyright (c) 2018 Metalurgi
Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

Refbacks

  • There are currently no refbacks.